Incoloy 901

  • The Incoloy 901 provided by Wenzhou Taixin Stainless Steel Co.,Limited enjoys a good reputation in the international market.We welcome you place trial order to test our quality.

 

  • If you are planning to buy Incoloy 901 from professional manufacturers suppliers in China, please feel free to contact Wenzhou Taixin Stainless Steel Co.,Ltd, equipped with productive factory, we are always at your service.

 

 

 

UNSTrademark
N09901Incoloy901
Chemical Composition:
Grade%NiCrCMnFeCo
Incoloy 901Min4011Rest
Max45140.111
SiCuMoSAlTiPB
52.350.01
0.60.570.030.353.10.030.02
Physical Performance:
Density8.14 g/cm3
Smelt1280-1345
Heat TreatmentT*SY*SEl
Rm N/mm2RP0.2N/mm2A5 %
-103468912


 

 Nickel alloy Incoloy 901 Chemical composition:

Alloy

%

Ni

Cu

Al 

Fe

Ti

Co

Mn

S

C

Si

P

Cr

Mo

B

Incoloy 901

Min.

40.0

2.35

11.0

5.0

0.01

Max.

45.0

0.50

0.35

Balance

3.10

1.0

1.0

0.03

0.10

0.60

0.03

14.0

7.0

0.02


Incoloy 901 Physical properties:

Density

8.14 g/cm3

Melting point

1280-1345°C


Incoloy 901 minimum mechanical properties in the room temperature:

Status

Tensile strength
Rm N/mm2

Yield strength
RP0.2N/mm2

Elongation
A5 %

Incoloy 901

1034

689

12


Description

A nickel-iron-chromium alloy containing titanium and aluminum for precipitation hardening and molybdenum for solid-solution strengthening. The alloy has high yield strength and creep resistance at temperatures to about 1110°F (600°C). A subtantial iron content enables the alloy to combine high strength with good forging characteristics. Used in gas turbines for discs and shafts. Standard products form is round.

Corrosion Resistance
Alloy 901 has good corrosion resistance to the atmospheres normally found in jet engine operations. It has slightly lower scaling resistance than such alloy as Types 309 and 310 stainless steel.

Workability 
Hot Working
Alloy 901 is forged between 2050°F (1121°C) and 1850°F (1010°C), metal temperature. Light hot work may be continued down to 1600°F (871°C) but not below. Metal temperature should not exceed 2050°F (1121°C) during rapid working. Billets should be charged into a hot furnace and heated rapidly through the precipitation hardening range.
 Weldability
Alloy 901 can be welded by the inert-gas-arc method. It is difficult to weld. All welding should be done in the solution treated condition. Cold worked parts should be re-solution treated before welding. A re-solution treatment is recommended after welding before stabilizing and aging.

 

 

Packing:

All our products are packed, stored, transported according to the international regulation. The products are wrapped with anti-rust paper and steel rings to prevent damage. Identification labels are tagged according to standard specification or customer's instructions. Special packing is available as per customer's requirement.Ply wooden box are available for special protection. Other kinds of packing can be offered if request.